Rustoleum Noxyde Pegarust Elastic Coating for Cladding
-18602-p.png?v=33F929F9-68EA-40B2-A248-0A2913D3CB53)
-18602-p.png?v=EBB3ADD7-E4C0-484C-A933-6C7AF13CDCA7)
-18602-p.png?v=D4464ED0-B121-4F28-A26D-255DDA5E8872)
Noxyde Pegarust is Back...
Rust-Oleum Noxyde Pegarust Elastic Coating for Cladding. Professional / Industrial use only.
Rust-Oleum Noxyde Pegarust is a single pack, rust preventing cladding coating for iron, steel, special alloys, galvanised and metallised iron and steel, aluminium, copper, zinc and lead, among other substrates. Pegarust is the solvent-based version of Noxyde, it comes with up to 5 years guarantee and it can be applied in temperatures as low as 0°C or on damp surfaces.
Noxyde Pegarust is a primer and topcoat in one and can be applied direct to various metallic substrates. It guarantees durable protection through its unique elastic and waterproofing binder technology. It offers outstanding adhesion even on moist surfaces and in damp weather.
Note: no longer atomised sprayable
Application by Brush, roller or airless spray systems.
Benefits:
- Excellent corrosion protection and waterproofing
- 5 year product warranty option (subject to site visit prior to the job starting). Call 01753 686888 for paint system advice
- Applicable in temperatures down to 0°C or on damp surfaces
- Protects against cracking and peeling
- Prevents rust spreading
- Suitable for corrosion class C5-M according to ISO 12944 (see certificate)
- UV-resistant and protects against abrasion
- Ultimate corrosion protection, even in low temperatures or on damp surfaces
- Excellent resistance against chemical agents in the atmosphere
- Protects against cracking and peeling
- Suitable for corrosion class C5-M according to ISO 12944
- Primer and topcoat in one
- Suitable for commercial buildings such as those occupied by major retail chains, car dealerships and fast food restaurants etc.
- Density: 1.15g/l
- Gloss level: Satin
- Corrosion class: C5 very high protection
- Solids content in volume: 46%
- Solids content in weight: 55%
- Drying times at 20°C/RH 50%: dry to recoat: 24-48 hours; fully cured: 1 week
- Recommended wet film thickness: 345 microns
- Recommended dry film thickness: 160 microns
- Theoretical consumption: 2.9m²/l per coat (it is recommended to apply 2 coats)
- Practical consumption: practical coverage depends on many factors such as porosity and roughness of the substrate and material losses during application
- Surface preparation: degrease if necessary. Derust substrate according to the conventional derusting techniques (sandblasting Sa2 and mechanical sanding St3). On a humid substrate, apply the first coat by brush or roller.
- To ensure homogeneity, coating materials should be thoroughly stirred prior to use
- Application conditions: May be applied in humid weather conditions
- Minimum ambient temperature: -5°C
- Application & thinning:
- Brush - apply undiluted
- Roller - apply undiluted
- Cleaning of equipment/spills: Thinner 22
- On new galvanised surfaces and new zinc first apply a coat of Metal Cladding Primer or PVDF Primer
- VOC level: 500 g/l
- VOC readymix: 500 g/l
- VOC category: A/i
- VOC limit: 500 g/l
- Flashpoint: 28°C
- Consult Safety Data Sheet and Safety Information printed on the can.
Customer reviews